The main raw material of wear-resistant ceramic tile is alumina, which is divided into 95%, 92%, 90% according to the alumina content.

Characteristic:

1. High hardness.

After testing, Rockwell hardness is as high as HR82-90.

2. Good wear resistance.

Wear resistance is significantly higher than wear-resistant steel and stainless steel.

3. Good impact resistance.

The compressive strength is above 200 MPa and the flexural strength is above 40 MPa, which can withstand long-term drilling erosion.

4. Can be firmly adhered.

It is bonded to the inner wall of the pipeline with a high temperature resistant adhesive, which can be used for a long time at room temperature.

5. Light weight.

The product density is 3.6g/cm3 and the weight is less than 1/2 of steel, which can greatly reduce the equipment load.